1. High film thickness, fast curing of various colors 2. Good adhesion, no need for primer, excellent adhesion to human nails 3. Good toughness, no cracking when bent at about 90° 4. Resistant to alcohol wiping 20-30 times 5. Anti-scratch, wear-resistant, high hardness and good protection |
|
6. The reaction is non-exothermic 7. Bright color, no yellowing 8. High gloss and fullness 9. Low skin irritation 10. Solution nail removal |
|
Supplier |
Item |
Type |
%bw |
Specialty |
|
U-SUNNY |
Trust 7050 |
Resin |
42 |
Excellent adhesion and excellent toughness |
|
U-SUNNY |
Trust 7080 |
Resin |
28 |
Quick drying, scratch and wear resistant |
|
U-SUNNY |
FM362 |
monomers |
13 |
Quick drying and strong dilution power |
|
lubrizol |
28000 |
Disperser |
0.2 |
Pigment dispersion |
|
tego |
245 |
Wetting Agent |
0.2 |
Wetting and leveling |
|
tego |
920 |
Defoamer |
0.3 |
defoaming |
|
DIC |
Pink E |
Pigment |
3 |
Red pigment, high coverage |
|
Sachtleben |
Micro |
Filler |
4 |
Color development, cost reduction, hardening filling |
|
Shamrock |
Fs421 |
Deurex |
1 |
Anti-scratch and wear-resistant |
|
ciba |
TPO |
Photoinitiator |
2 |
initiator |
|
ciba |
907 |
Photoinitiator |
4.5 |
long wave initiator |
|
ciba |
ITX |
Photoinitiator |
1.5 |
co-initiator |
|
TOTAL |
|
|
100% |
|
Recipe design :
Test conditions: 9W blue LED light source, wavelength 415nm
Film thickness 60-80um (coated on release film peeling test)
Performance:
A. The film thickness of 60um cures quickly, and the surface dries in 60 seconds after curing in 30 seconds.
B. Excellent adhesion to human nails
C. Flexibility bending test >120 degrees without bursting
D. 99.8% analytical pure alcohol 500g force rubbing test, no discoloration and matte phenomenon
E. No obvious exothermic phenomenon
F. Bright colors and no yellowing phenomenon
G. High gloss, high fullness, tested at 65° angle, gloss >96°
H. Low skin irritation, no bad odor
I. Nail nail remover is easy to clean